Graphite Crucible 

Bulk Density  1.85 g/cm3        Electric Resistivity  15unm    Ash  0.1%

Bending strength  65 mpa       Resist Compression  60mpa   Particle 43um                  

Application :

Gold, Silver, Copper, Aluminum, Sterling Silver, Bullion,Tin, Zinc, Lead  melting or 

casting particular amorphous metals, rare metals and non-ferrous metals or alloys in MF Series and 

Hardin Melting Furnaces ,Digital Electric Smelting Furnaces,  hand held melting furnace...

Designed with grooved flange for crucible tongs and pour spout for easy pouring applications.

Size Sheet

The crucible is equipped with pouring spout and double flanges.

Notes

1. Graphite crucible should be kept away from humid environment, and must be stored in a dry place or on a wooden shelf.

2. Handle it with care. Falling or shaking is strictly forbidden.

3. Roast it in drying equipment or by a furnace before use, wait till its temperature gradually rises to 500°C.

4. Crucible should be placed below the mouth of furnace to prevent the furnace lid abrading the upper edge of the crucible.

5. Feed materials according to the smelting capacity of crucible. It is not allowed to feed too many materials, in order to avoid crucible swelling.

6. The furnace discharging tools and clamps should comply with the shape of the crucible, 

and use the tools to clamp the middle section of the crucible to prevent local stress from damaging the crucible.

7. Knock the crucible gently while removing slags and sticky cokes on the internal and external wall of the crucible. Don't strike it heavily.

8. Keep appropriate distance between the crucible and the furnace wall. The crucible should be placed in the middle of the furnace.

9. Excessive use of combustion improver and additives will reduce the service life of crucible.

10. Rotate the crucible every week to extend its service life.

11. Prevent strong oxidation flame from reaching the side and bottom of the crucible directly.